Evaluation of the porosity of ornamental glazed tiles by nitrogen adsorption

The adsorption of nitrogen at 77 K has been carried out on samples of Portuguese ornamental glazed tiles (azulejos) from the XVIth to XXth centuries. Analysis of the results indicates that degradation is associated with the development of mesoporosity and an increase in specific surface area. It was found that impregnation of deteriorated tiles with Paraloid...

Πλήρης περίληψη

Αποθηκεύτηκε σε:
Κύριοι συγγραφείς: Ribeiro Carrott M.M.L., Farinha Antunes J.L., Carrott P.J.M.
Συλλογικό Έργο: International symposium on the conservation of monuments in the Mediterranean, International Group on the Conservation of Monuments in the Mediterranean Basin (I.G.C.M.M.), Community of Mediterranean Univ., ΕΜΠ, European Commission - Directorate General X, Intern. Centr. of Mediterranean Studies, Νομαρχία Δωδεκανήσου, Δήμος Ρόδου, ΤΕΕ - Τμ. Δωδεκανήσου
Κατηγορία Υλικού: Εισήγηση συνεδρίου
Γλώσσα: Αγγλικά
Γλώσσα περίληψης: Αγγλικά
Στοιχεία έκδοσης: ΤΕΕ , 1997
Πηγή:Νέες αντιλήψεις,τεχνολογίες και υλικά για τη συντήρηση και διαχείριση ιστορικών πόλεων και συνόλων (4ο:1997:Ρόδος, Ελλάδα) / / ed. A. Moropoulou, E. Zezza, E. Kollias, I. Papachristodoul . τ.3
Θέματα:
Γενική θεματική ενότητα:ΑΡΧΙΤΕΚΤΟΝΙΚΗ
Διαδίκτυο:Το πλήρες κείμενο
Φυσική περιγραφή:vol.3, pp.79-87 : fig., tabl.
Βιβλιογραφία:Biblgr.:pp.86-87
Εκδότης:ΤΕΕ
Περίληψη:The adsorption of nitrogen at 77 K has been carried out on samples of Portuguese ornamental glazed tiles (azulejos) from the XVIth to XXth centuries. Analysis of the results indicates that degradation is associated with the development of mesoporosity and an increase in specific surface area. It was found that impregnation of deteriorated tiles with Paraloid B-72 or with polyurethane was effective in blocking the porosity. Wacker OH, on the other hand, did not cause blocking of the pores but appeared to be deposited as a surface coating. It is concluded that the technique of low temperature nitrogen adsorption is very useful for characterising porosity, and its changes during degradation or after consolidation procedures, in a region of pore size where other techniques are inadequate. (AU)
ISBN:960-7018-59-1 (set)
960-7018-62-1 (τ.3)
Κωδικός DEWEY:721.0443 - (Πλακάκια:Δομικά στοιχεία:Αρχιτεκτονικός σχεδιασμός)
720.288 - (Συντήρηση μνημείων:Αρχιτεκτονική)
721.0288 - (Αποκατασταση μνημειων:Αρχιτεκτονικος σχεδιασμος)
DEWEY Γενικού θέματος:720 - (ΑΡΧΙΤΕΚΤΟΝΙΚΗ)